Author(s): Guimarães Junior, José Benedito ; Protásio, Thiago de Paula ; Mendes, Rafael Farinassi ; Mendes, Lourival Marin ; Guimarães, Bárbara Maria Ribeiro ; de Siqueira, Humberto Fauller
Date: 2015
Origin: Oasisbr
Subject(s): Physical and mechanical properties; Laminated panels; Resorcinol-formaldehyde; Propriedades físicas e mecânicas; Painéis laminados; Resorcinol-formaldeído
The objective of this research was to verify the quality of LVL panels manufactured with wood of five clones of Eucalyptus urophylla. Five LVL panels were produced for each clone, with 2 mm veneer, resorcinol-formaldehyde adhesive with a 320 g m-² weight, 1.47 MPa pressure for a period of 8 h at room temperature. In general, all clones showed potential to be used for production of LVL panels, especially clone 26, as it showed better performance regarding physical properties and bonding strength.
O objetivo deste trabalho foi verificar a qualidade de painéis LVL produzidos com a madeira de cinco clones de Eucalyptus urophylla. Para cada clone foram produzidos cinco painéis LVL, com lâminas de 2 mm de espessura, adesivo resorcinol-formaldeído com gramatura de 320 g m-², pressão de 1,47 MPa durante o período de 8 h a temperatura ambiente. De maneira geral, todos os clones apresentaram potencial para a produção de painéis LVL, com destaque para o clone 26, por apresentar melhor desempenho com relação às propriedades físicas e resistência à colagem.