Autor(es): Yaqub, Talha Bin ; Yaqoob, Khuram ; Mukhtar, Amir ; Fernandes, Filipe ; Bondarev, Andrey ; Ferreira, Fabio ; Al-Rjoub, Abbas ; Cavaleiro, Albano
Data: 2022
Identificador Persistente: http://hdl.handle.net/10400.22/22011
Origem: Repositório Científico do Instituto Politécnico do Porto
Assunto(s): W-S-N films; Solid lubricants; Friction and wear; DC magnetron sputtering
This work deals with the investigation of the tribological performance of DC magnetron sputteredW-S-N coatings under vacuum atmosphere, as part of the exploration of multi-environment sliding properties of W-S-N solid lubricants. This study is part of the systematic testing of W-S-N solid lubricants in different environments, especially vacuum, which is often ignored. The trend is to test sliding properties in dry N2 by considering it as replacement of vacuum environment testing. This approach is not appropriate. In this work, a set of coatings was synthesized with N-alloying content in the range of 0–25.5 at.%. A maximum S/W ratio of 1.47 was observed for the pure WSx coating. A maximum hardness of 8.0 GPa was observed for 23 at.% of N-alloying. The coating with the lowest N content (14.6 at.%) displayed the lowest friction, specific wear rate and wear scar depth under vacuum conditions. Despite superior sliding performance at room temperature (35% humidity), 200 C and dry nitrogen conditions, the performance of the WSN12.5 coating deteriorated vacuum environment.