Document details

Submitted by Simone Maisonave (simonemaisonave@hotmail.com) on 2020-05-14T20:34:12Z No. of bitstreams: 2 license_rdf: 0 bytes, checksum: d41d8cd98f00b204e9800998ecf8427e (MD5) Veronica Coffy Bilhalba_Dissertacao.pdf: 2822740 bytes, checksum: 4ce71d8c6913e2c1363a8ed67dd6a1dc (MD5)

Approved for entry into archive by Aline Batista (alinehb.ufpel@gmail.com) on 2020-05-16T03:45:22Z (GMT) No. of bitstreams: 2 Veronica Coffy Bilhalba_Dissertacao.pdf: 2822740 bytes, checksum: 4ce71d8c6913e2c1363a8ed67dd6a1dc (MD5) license_rdf: 0 bytes, checksum: d41d8cd98f00b204e9800998ecf8427e (MD5)

Made available in DSpace on 2020-05-16T03:45:22Z (GMT). No. of bitstreams: 2 Veronica Coffy Bilhalba_Dissertacao.pdf: 2822740 bytes, checksum: 4ce71d8c6913e2c1363a8ed67dd6a1dc (MD5) license_rdf: 0 bytes, checksum: d41d8cd98f00b204e9800998ecf8427e (MD5) Previous issue date: 2014-03-31

O presente trabalho apresenta um método alternativo para a restauração de cerâmicas que, se comparado às outras práticas desenvolvidas na atualidade, promete facilidades à etapa de recomposição estrutural. Trata-se de um produto composto de materiais geralmente mencionados na literatura do restauro, tais como cargas minerais e emulsão de poliacetato de vinil (PVA), que é processado por radiação em um forno de micro-ondas convencional. A massa polivinílica proposta foi idealizada a partir da composição de massas cerâmicas de dois objetos escolhidos para o estudo de restauro. Os objetivos principais da pesquisa foram analisar o desempenho técnico do material experimental, durante e depois do trabalho de restauração, e de verificar o efeito das micro-ondas nas misturas polivinílicas, uma vez que o compósito adesivo é descrito na literatura como material suscetível à (foto) oxidação e acidificação quando submetido à energia calorífera ou fonte de irradiação. Dentro dessa perspectiva, a etapa experimental envolveu o acompanhamento de amostras durante sua secagem e em embalagem plástica, ensaios de aplicação das massas, testes de revestimento e de remoção, exames de caracterização por microscopia óptica (MO), microscopia eletrônica de varredura (MEV), espectrometria de energia dispersiva de raios X (EDX), ensaios de reometria (ensaio de flexão), termogravimetria (TGA e D-TGA) e espectroscopia de infravermelho por transformada de Fourier (FTIR). Os testes práticos demonstraram que o material experimental corresponde aos princípios práticos da restauração contemporânea, já que é de fácil produção, aplicação, remoção, distinguibilidade, além de ser adaptável à composição dos objetos em restauro. As análises instrumentais indicaram qualidades físicas e estabilidade para as massas polivinílicas irradiadas. Apesar dos resultados promissores, a pesquisa não oferece parecer conclusivo, uma vez que o material experimental não pôde ser submetido ao ensaio de envelhecimento acelerado.

This work presents an alternative method for the ceramics restoration that, compared to other practices developed nowadays, promises facilities for structural rearrangement step. It is a product composed of materials generally mentioned in the restoration literature, such as mineral fillers and emulsion of Polyvinyl Acetate (PVA), which is processed by radiation in a conventional microwave oven. The mass polyvinyl proposal was designed from the composition of ceramic masses of two objects chosen for the study of restoration. The main objectives of the research were to analyze the technicç.d1l tr 1\NB Spçal performance of the experimental material, during and after the restoration work, and check the effect of microwave on polyvinyl mixtures, since the adhesive composite is described in the literature as the material susceptible to the photo-oxidation and acidification when subjected to the calorific energy or radiation source. Within this perspective, experimental step involved the monitoring of samples during drying and plastic packaging, application essays masses, coating and removal tests, exams characterization by optical microscopy (OM), scanning electron microscopy (SEM), energy dispersive spectrometry X-ray (EDX), mechanical rheometry (bending test), thermogravimetry (TGA and D-TGA) and Fourier Transform Infrared Spectroscopy (FTIR). The practical tests demonstrated that the experimental material corresponds to practice principles of contemporary restoration, since it is easy to produce, application, removal, distinctiveness, and is adaptable to restore composition of objects. Instrumental analyzes indicated physical qualities and stability for the polyvinyl masses irradiated. Despite the promising results, the research does not provide conclusive, since the experimental material could not be subjected to the accelerated aging test.