Autor(es): Mestieri, Leticia Boldrin [UNESP] ; Tanomaru-Filho, Mário [UNESP] ; Gomes-cornélio, Ana Livia [UNESP] ; Salles, Loise Pedrosa [UNESP] ; Bernardi, Maria Inês Basso ; Guerreiro-Tanomaru, Juliane Maria [UNESP]
Data: 2015
Identificador Persistente: http://hdl.handle.net/11449/126198
Origem: Oasisbr
Assunto(s): Silicate cement; Niobium; Nanotechnology; Silicate cement; Silicate cement; Niobium; Niobium; Nanotechnology; Nanotechnology
Made available in DSpace on 2015-08-06T16:14:48Z (GMT). No. of bitstreams: 0 Previous issue date: 2014-12-01. Added 1 bitstream(s) on 2015-08-06T16:44:20Z : No. of bitstreams: 1 S1678-77572014000600554.pdf: 2194673 bytes, checksum: 018c479d8933d36cc1fe2878646b3c56 (MD5)
Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)
ObjectiveMineral Trioxide Aggregate (MTA) is composed of Portland Cement (PC) and bismuth oxide (BO). Replacing BO for niobium oxide (NbO) microparticles (Nbµ) or nanoparticles (Nbη) may improve radiopacity and bioactivity. The aim of this study was to evaluate the radiopacity and cytotoxicity of the materials: 1) PC; 2) White MTA; 3) PC+30% Nbµ; 4) PC+30% Nbη. Material and MethodFor the radiopacity test, specimens of the different materials were radiographed along an aluminum step-wedge. For cell culture assays, Saos-2 osteoblastic-cells (ATCC HTB-85) were used. Cell viability was evaluated through MTT assay, and bioactivity was assessed by alkaline phosphatase activity assay. ResultThe results demonstrated higher radiopacity for MTA, followed by Nbµ and Nbη, which had similar values. Cell culture analysis showed that PC and PC+NbO associations promoted greater cell viability than MTA. ConclusionIt was concluded that the combination of PC+NbO is a potential alternative for composition of MTA.