Detalhes do Documento

Descrição

Made available in DSpace on 2015-12-07T15:30:35Z (GMT). No. of bitstreams: 0 Previous issue date: 2014. Added 1 bitstream(s) on 2015-12-07T15:53:01Z : No. of bitstreams: 1 S0103-64402014000300212.pdf: 186565 bytes, checksum: 56112b29a689f2fde6dc5e565fce079a (MD5)

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Este estudo avaliou a difusão de íons hidroxila de diferentes pastas de hidróxido de cálcio contendo Aloe vera através dos túbulos dentinários. Foram utilizados 60 dentes bovinos unirradiculares. As coroas dos dentes foram removidas, os canais radiculares foram instrumentados e divididos em 4 grupos (n=15) de acordo com a medicação intracanal: Grupo HC/ SF – pasta de hidróxido de cálcio e soro fisiológico; Grupo HC/P – pasta de hidróxido de cálcio e propilenoglicol; Grupo HC/A – pasta de hidróxido de cálcio e Aloe vera gel; Grupo HC/A/P – pasta de hidróxido de cálcio, propilenoglicol e Aloe vera. Após o preenchimento dos canais radiculares com as respectivas pastas, os dentes foram selados coronalmente e na região do ápice radicular com adesivo epóxi. Os dentes foram colocados em frascos identificados contendo água deionizada e armazenados em estufa, com 100% de umidade, a 37°C. Após 3h, 24h, 72h, 7 dias, 15 dias e 30 dias, a água deionizada dos frascos foi coletada e realizada a medição do pH com auxílio de um pHmetro. Os dados obtidos foram submetidos à análise estatística, com grau de significância de 5%. Os resultados mostraram que todas as pastas estudadas promoveram a difusão dos íons hidroxila através dos túbulos dentinários. A associação do Aloe vera ao HC (grupo HC/A) resultou em uma liberação de forma constante de íons cálcio. O grupo HC/A/P mostrou o pH mais elevado que as demais pastas em 24 e 72 horas. Concluiu-se que as pastas experimentais contendo Aloe vera foram capazes de permitir a difusão de íons hidroxila através dos túbulos dentinários.

This study evaluated the diffusion through the dentinal tubules of hydroxyl ions from different calcium hydroxide (CH) pastes containing Aloe vera. Sixty single-rooted bovine teeth were used. The tooth crowns were removed, the root canals were instrumented and the specimens were assigned to 4 groups (n=15) according to the intracanal medication: Group CH/S - CH powder and saline paste; Group CH/P - CH powder and propylene glycol paste; Group CH/A - calcium hydroxide powder and Aloe vera gel paste; Group CH/A/P - CH powder, Aloe vera powder and propylene glycol paste. After placement of the root canal dressings, the teeth were sealed coronally and apically with a two-step epoxy adhesive. The teeth were placed in identified flasks containing deionized water and stored in an oven with 100% humidity at 37 °C. After 3 h, 24 h, 72 h, 7 days, 15 days and 30 days, the deionized water in the flasks was collected and its pH was measured by a pH meter. The obtained data were subjected to statistical analysis at a significance level of 5%. The results demonstrated that all pastes provided diffusion of hydroxyl ions through the dentinal tubules. The combination of Aloe vera and CH (group CH/A) provided a constant release of calcium ions. Group CH/A/P showed the highest pH at 24 and 72 h. In conclusion, the experimental pastes containing Aloe vera were able to enable the diffusion of hydroxyl ions through the dentinal tubules.

Departamento de Materiais Odontológicos e Prótese, Faculdade de Odontologia de Araçatuba (FOA), Universidade Estadual Paulista (UNESP), Araçatuba, SP, Brasil

Private Practice, São Paulo, SP, Brasil

Departamento de Clínica Integrada, Faculdade de Odontologia de Adamantina, Faculdades Adamatinenses Integradas (FAI), Adamantina, SP, Brasil

Universidade Estadual Paulista, Departamento de Materiais Odontológicos e Prótese, Faculdade de Odontologia de Araçatuba

FAPESP: 2011/20257-0