Autor(es):
Kuroda, P. A.B. [UNESP] ; Lourenço, M. L. [UNESP] ; Correa, D. R.N. ; Grandini, C. R. [UNESP]
Data: 2020
Identificador Persistente: http://hdl.handle.net/11449/201176
Origem: Oasisbr
Assunto(s): Mechanical properties; Metallic biomaterial; Microstructure; Thermomechanical treatments; Ti alloys; Mechanical properties; Mechanical properties; Metallic biomaterial; Metallic biomaterial; Microstructure; Microstructure; Thermomechanical treatments; Thermomechanical treatments; Ti alloys; Ti alloys
Descrição
Made available in DSpace on 2020-12-12T02:26:00Z (GMT). No. of bitstreams: 0 Previous issue date: 2020-01-05
Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)
Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)
The study and development of new titanium alloys aim to place a metallic biomedical device with better mechanical compatibility with the bone, that is, with a smaller Young's modulus, on the market, to improve its application in the orthopedic and dental fields. This study analyzed the influence of thermomechanical treatments on the structure, hardness, and elastic modulus of the Ti–20Zr–Mo ternary alloy system, where the molybdenum content varied between 0 and 10 wt%. The treatments performed in this study involved homogenization, hot-rolling, and annealing. The structural and microstructural analyses were performed by X-ray diffraction, optical and scanning electron microscopy. An analysis of the mechanical properties of the alloy was obtained by measuring Vickers microhardness and the dynamic elastic modulus. The structural and microstructural results indicated that the Ti–20Zr alloy has only the α′ phase, the Ti–20Zr–10Mo alloy had a predominance of β phase, and the other alloys were α+β types. The hardness increased due to solid-state hardening with the increase of the molybdenum content and due to hot-rolling processing, which increased the internal stresses of the material. The elastic modulus decreased with higher levels of molybdenum and the hot-rolling processing, due to β phase stabilization. The other treatments increased the elastic modulus and may even induce the formation of the omega phase in some alloys of the system.
UNESP – Univ. Estadual Paulista Laboratório de Anelasticidade e Biomateriais, 17.033.360
IBTN – Br Institute of Biomaterials Tribocorrosion and Nanomedicine, Brazilian Branch, 17.033.360
IFSP – Federal InstituteofEducation Science and Technology of São Paulo Grupo de Pesquisa em Materiais Metálicos Avançados
UNESP – Univ. Estadual Paulista Laboratório de Anelasticidade e Biomateriais, 17.033.360
FAPESP: 2012/22742-6
FAPESP: 2015/09480-0
CNPq: 307279/2013-8