Reverse shape selectivity in the adsorption of hexane and xylene isomers in MOF UiO-66

Ver documento

Detalhes bibliográficos
Resumo:An adsorption study of hexane and xylene isomers mixtures was addressed in a rigid zirconium terephthalate UiO-66 (UiO for University of Oslo) with octahedral and tetrahedral cavities of free diameter close to 1.1 nm and 0.8 nm, respectively. Multicomponent equimolar breakthrough experiments show that the adsorption hierarchy of structural isomers in UiO-66 is opposite to the one observed in conventional adsorbents. For hexane isomers, it was found that the amount adsorbed increases with the degree of branching, being 2,2-dimethylbutane (22DMB) and 2,3-dimethylbutane (23DMB) the more retained molecules. Regarding the xylene isomers, the results show that the adsorption of the bulkier ortho-xylene(oX) is favoured compared to its homologues. The structural similarity between MOF UiO-66 and zeolite MCM-22 suggests that the reverse shape selectivity observed in the adsorption of hexane and xylene isomers might be attributed to the rotational freedom of the molecules inside the small cavities.
Autores principais:Silva, José A.C.
Outros Autores:Rodrigues, Alírio; Bárcia, Patrick da Silva; Guimarães, Daniela; Mendes, Patricia; Chevreau, Hubert; Serre, Christian; Guillerm, Vincent
Assunto:MOFs Hexane isomers Adsorption
Ano:2011
País:Portugal
Tipo de documento:artigo
Tipo de acesso:acesso aberto
Instituição associada:Instituto Politécnico de Bragança
Idioma:inglês
Origem:Biblioteca Digital do IPB