Corrosion and tribocorrosion behaviour of beta-type Ti-Nb and Ti-Mo surfaces designed by diffusion treatments for biomedical applications
| Resumo: | Corrosion and tribocorrosion behaviour of modified Ti surfaces through thermochemical treatments has been studied. Electrochemical Impedance Spectroscopy (EIS) and reciprocating sliding tests using a ball-on-plate tribometer under 1 N load and alumina as counter-material were used to evaluate the influence of Nb and Mo on titanium corrosion and tribocorrosion properties.Ti-Nb and Ti-Mo surfaces exhibited better anticorrosive properties than CP-titanium. Under tribological action the modified Ti surfaces showed similar coefficient of friction and lower tendency to corrosion compared to CP-Ti. Furthermore, Nb diffusion increased the repassivation rate with respect to Ti and Ti-Mo surfaces due to its stable passive film. |
|---|---|
| Autores principais: | Urena, J. |
| Outros Autores: | Tsipas, S.; Pinto, A. M. P.; Toptan, Fatih; Gordo, E.; Jimenez-Morales, A. |
| Assunto: | beta-Gradient titanium Powder technology Nb and Mo surface treatments Corrosion Tribocorrosion β-Gradient titanium |
| Ano: | 2018 |
| País: | Portugal |
| Tipo de documento: | artigo |
| Tipo de acesso: | acesso aberto |
| Instituição associada: | Universidade do Minho |
| Idioma: | inglês |
| Origem: | RepositóriUM - Universidade do Minho |
| Resumo: | Corrosion and tribocorrosion behaviour of modified Ti surfaces through thermochemical treatments has been studied. Electrochemical Impedance Spectroscopy (EIS) and reciprocating sliding tests using a ball-on-plate tribometer under 1 N load and alumina as counter-material were used to evaluate the influence of Nb and Mo on titanium corrosion and tribocorrosion properties.Ti-Nb and Ti-Mo surfaces exhibited better anticorrosive properties than CP-titanium. Under tribological action the modified Ti surfaces showed similar coefficient of friction and lower tendency to corrosion compared to CP-Ti. Furthermore, Nb diffusion increased the repassivation rate with respect to Ti and Ti-Mo surfaces due to its stable passive film. |
|---|