Comparative Study of Pure Mg and AZ91D as Sacrificial Anodes for Reinforced Cement Concrete Structures in a Chloride Atmosphere
| Resumo: | A comparative study of the corrosion behavior of pure magnesium and AZ91D anodes in reinforced cement concrete was undertaken in the present work. The steel reinforcements were electrochemically kept in contact with these anodes in a chloride atmosphere, and the half-cell potential drop was observed. Bare steel reinforcements were tied to the anodes and were also kept in a high chloride atmosphere to test the mechanical properties. The yield stress and ultimate tensile stress were found to decrease by approximately 50 MPa, while the reduction in percentage elongation was approximately 25% for reinforcements tied to AZ91D and pure Mg, at the end of 80 days, compared to the fresh steel reinforcement. The rate of corrosion of pure Mg was reportedly slightly higher compared to AZ91D, due to the presence of inter-metallics, as inferred through micro-graphs. |
|---|---|
| Autores principais: | Murthy,Yogesh Iyer |
| Outros Autores: | Gandhi,Sumit; Kumar,Abhishek |
| Assunto: | cathodic protection AZ91D mechanical properties half-cell potential micro-characterization inter-metallics |
| Ano: | 2020 |
| País: | Portugal |
| Tipo de documento: | artigo |
| Tipo de acesso: | acesso aberto |
| Instituição associada: | Fundação para a Ciência e Tecnologia |
| Idioma: | inglês |
| Origem: | SciELO Portugal |
| _version_ | 1868441723803271168 |
|---|---|
| author | Murthy,Yogesh Iyer |
| author2 | Gandhi,Sumit Kumar,Abhishek |
| author2_role | author author |
| author_facet | Murthy,Yogesh Iyer Gandhi,Sumit Kumar,Abhishek |
| author_role | author |
| country_str | PT |
| creators_json_txt | [{\"Person.name\":\"Murthy,Yogesh Iyer\"},{\"Person.name\":\"Gandhi,Sumit\"},{\"Person.name\":\"Kumar,Abhishek\"}] |
| datacite.creators.creator.creatorName.fl_str_mv | Murthy,Yogesh Iyer Gandhi,Sumit Kumar,Abhishek |
| datacite.rights.fl_str_mv | http://purl.org/coar/access_right/c_abf2 |
| datacite.subjects.subject.fl_str_mv | cathodic protection AZ91D mechanical properties half-cell potential micro-characterization inter-metallics |
| datacite.titles.title.fl_str_mv | Comparative Study of Pure Mg and AZ91D as Sacrificial Anodes for Reinforced Cement Concrete Structures in a Chloride Atmosphere |
| dc.creator.none.fl_str_mv | Murthy,Yogesh Iyer Gandhi,Sumit Kumar,Abhishek |
| dc.format.none.fl_str_mv | text/html |
| dc.identifier.none.fl_str_mv | http://scielo.pt/scielo.php?script=sci_arttext&pid=S0872-19042020000400004 |
| dc.language.none.fl_str_mv | eng |
| dc.publisher.none.fl_str_mv | Sociedade Portuguesa de Electroquímica |
| dc.rights.none.fl_str_mv | http://purl.org/coar/access_right/c_abf2 |
| dc.source.none.fl_str_mv | Portugaliae Electrochimica Acta v.38 n.4 2020 |
| dc.subject.none.fl_str_mv | cathodic protection AZ91D mechanical properties half-cell potential micro-characterization inter-metallics |
| dc.title.fl_str_mv | Comparative Study of Pure Mg and AZ91D as Sacrificial Anodes for Reinforced Cement Concrete Structures in a Chloride Atmosphere |
| dc.type.none.fl_str_mv | http://purl.org/coar/resource_type/c_6501 |
| description | A comparative study of the corrosion behavior of pure magnesium and AZ91D anodes in reinforced cement concrete was undertaken in the present work. The steel reinforcements were electrochemically kept in contact with these anodes in a chloride atmosphere, and the half-cell potential drop was observed. Bare steel reinforcements were tied to the anodes and were also kept in a high chloride atmosphere to test the mechanical properties. The yield stress and ultimate tensile stress were found to decrease by approximately 50 MPa, while the reduction in percentage elongation was approximately 25% for reinforcements tied to AZ91D and pure Mg, at the end of 80 days, compared to the fresh steel reinforcement. The rate of corrosion of pure Mg was reportedly slightly higher compared to AZ91D, due to the presence of inter-metallics, as inferred through micro-graphs. |
| dirty | 0 |
| eu_rights_str_mv | openAccess |
| format | article |
| id | scielopt_df85c07d21b166bddea39ad5fb0aee96 |
| identifier.url.fl_str_mv | http://scielo.pt/scielo.php?script=sci_arttext&pid=S0872-19042020000400004 |
| instacron_str | SciELO |
| institution | Fundação para a Ciência e Tecnologia |
| instname_str | Fundação para a Ciência e Tecnologia |
| language | eng |
| network_acronym_str | scielopt |
| network_name_str | SciELO Portugal |
| oai_identifier_str | oai:scielo:S0872-19042020000400004 |
| organization_str_mv | urn:organizationAcronym:scielo |
| person_str_mv | Murthy,Yogesh Iyer Gandhi,Sumit Kumar,Abhishek |
| publishDate | 2020 |
| publisher.none.fl_str_mv | Sociedade Portuguesa de Electroquímica |
| reponame_str | SciELO Portugal |
| repository_id_str | urn:repositoryAcronym:scielopt |
| service_str_mv | urn:repositoryAcronym:scielopt |
| spelling | Comparative Study of Pure Mg and AZ91D as Sacrificial Anodes for Reinforced Cement Concrete Structures in a Chloride AtmosphereMurthy,Yogesh IyerGandhi,SumitKumar,Abhishekcathodic protectionAZ91Dmechanical propertieshalf-cell potentialmicro-characterizationinter-metallicsopen accesshttp://purl.org/coar/access_right/c_abf2http://scielo.pt/scielo.php?script=sci_arttext&pid=S0872-19042020000400004URLhttp://scielo.pt/scielo.php?script=sci_arttext&pid=S0872-19042020000400004URLHasVersion2020-06-01A comparative study of the corrosion behavior of pure magnesium and AZ91D anodes in reinforced cement concrete was undertaken in the present work. The steel reinforcements were electrochemically kept in contact with these anodes in a chloride atmosphere, and the half-cell potential drop was observed. Bare steel reinforcements were tied to the anodes and were also kept in a high chloride atmosphere to test the mechanical properties. The yield stress and ultimate tensile stress were found to decrease by approximately 50 MPa, while the reduction in percentage elongation was approximately 25% for reinforcements tied to AZ91D and pure Mg, at the end of 80 days, compared to the fresh steel reinforcement. The rate of corrosion of pure Mg was reportedly slightly higher compared to AZ91D, due to the presence of inter-metallics, as inferred through micro-graphs.Sociedade Portuguesa de ElectroquímicaPortugaliae Electrochimica Acta v.38 n.4 2020text/htmlengjournal articlehttp://purl.org/coar/resource_type/c_6501literature |
| spellingShingle | Comparative Study of Pure Mg and AZ91D as Sacrificial Anodes for Reinforced Cement Concrete Structures in a Chloride Atmosphere Murthy,Yogesh Iyer cathodic protection AZ91D mechanical properties half-cell potential micro-characterization inter-metallics |
| status | SINGLETON |
| subject.fl_str_mv | cathodic protection AZ91D mechanical properties half-cell potential micro-characterization inter-metallics |
| title | Comparative Study of Pure Mg and AZ91D as Sacrificial Anodes for Reinforced Cement Concrete Structures in a Chloride Atmosphere |
| title_full | Comparative Study of Pure Mg and AZ91D as Sacrificial Anodes for Reinforced Cement Concrete Structures in a Chloride Atmosphere |
| title_fullStr | Comparative Study of Pure Mg and AZ91D as Sacrificial Anodes for Reinforced Cement Concrete Structures in a Chloride Atmosphere |
| title_full_unstemmed | Comparative Study of Pure Mg and AZ91D as Sacrificial Anodes for Reinforced Cement Concrete Structures in a Chloride Atmosphere |
| title_short | Comparative Study of Pure Mg and AZ91D as Sacrificial Anodes for Reinforced Cement Concrete Structures in a Chloride Atmosphere |
| title_sort | Comparative Study of Pure Mg and AZ91D as Sacrificial Anodes for Reinforced Cement Concrete Structures in a Chloride Atmosphere |
| topic | cathodic protection AZ91D mechanical properties half-cell potential micro-characterization inter-metallics |
| topic_facet | cathodic protection AZ91D mechanical properties half-cell potential micro-characterization inter-metallics |
| url | http://scielo.pt/scielo.php?script=sci_arttext&pid=S0872-19042020000400004 |
| visible | 1 |