Potentiodynamic Polarization Behavior and Microscopic Examination of Tungsten Carbide Hard Metal Materials in Supported Ammoniacal Medium
| Resumo: | Electrochemical methods for the recycling of tungsten carbide (WC-10Co) resources suffer from passivation in the acidic medium caused by WO3 and also in NaOH electrolytes, due to hydroxide formation. We found that an ammoniacal solution is a promising electrolyte for sustainable electrochemical dissolution of both tungsten (W) and cobalt (Co). The ammoniacal medium performs greatly when supported with Cl-, SO4(2-) and CO3(2-) ions. Poor dissolution/corrosion tendency of WC-10Co in a diluted NH4OH solution enhanced many folds in the presence of Cl-, SO4(2-) and CO3(2-) ions. Among these supporting ions, Cl- emerged as the most suitable for the electrochemical leaching of W and Co from the WC-10Co, accompanying the least noble behavior of WC-10Co. An electrolyte composed of 150 g/L of ammonia and 5% (w/v) of NH4Cl yielded the maximum anodic current density. Microscopic examination of the electrochemically treated samples shows scattered active sites responsible for the oxidative dissolution of WC-10Co. The usefulness of W and Co dissolution in ammonia-additive salt followed the order NH4OH-NH4Cl>NH4OH-(NH4)2SO4>NH4OH-(NH4)2CO3. |
|---|---|
| Autores principais: | Randhawa,Navneet Singh |
| Outros Autores: | Katiyar,Prvan Kumar |
| Assunto: | ammoniacal electrolyte electroleaching electrodissolution potentiodynamic tungsten carbide |
| Ano: | 2020 |
| País: | Portugal |
| Tipo de documento: | artigo |
| Tipo de acesso: | acesso aberto |
| Instituição associada: | Fundação para a Ciência e Tecnologia |
| Idioma: | inglês |
| Origem: | SciELO Portugal |
| Resumo: | Electrochemical methods for the recycling of tungsten carbide (WC-10Co) resources suffer from passivation in the acidic medium caused by WO3 and also in NaOH electrolytes, due to hydroxide formation. We found that an ammoniacal solution is a promising electrolyte for sustainable electrochemical dissolution of both tungsten (W) and cobalt (Co). The ammoniacal medium performs greatly when supported with Cl-, SO4(2-) and CO3(2-) ions. Poor dissolution/corrosion tendency of WC-10Co in a diluted NH4OH solution enhanced many folds in the presence of Cl-, SO4(2-) and CO3(2-) ions. Among these supporting ions, Cl- emerged as the most suitable for the electrochemical leaching of W and Co from the WC-10Co, accompanying the least noble behavior of WC-10Co. An electrolyte composed of 150 g/L of ammonia and 5% (w/v) of NH4Cl yielded the maximum anodic current density. Microscopic examination of the electrochemically treated samples shows scattered active sites responsible for the oxidative dissolution of WC-10Co. The usefulness of W and Co dissolution in ammonia-additive salt followed the order NH4OH-NH4Cl>NH4OH-(NH4)2SO4>NH4OH-(NH4)2CO3. |
|---|