Cyclic plastic behaviour of 7075 aluminium alloy
| Resumo: | This paper aims at studying the cyclic plastic behaviour of the 7075-T651 aluminium alloy under fully-reversed strain-controlled conditions. Tests are conducted under strain-control mode, at room temperature, in a conventional servo-hydraulic machine, from smooth samples, using the single step method, with strain amplitudes (∆ε/2) in the range ±0.5 to ±2.75%. This material has exhibited a mixed behaviour, i.e. cyclic strain-hardens at higher strain amplitudes (∆ε/2/>1.1%) and cyclic strain-softens at lower strain amplitudes (∆ε/2<1.1%). A linear relationship between the degree of cyclic strain-hardening and the strain amplitude has been established for higher strain amplitudes. Fatigue-ductility and fatigue-strength properties agree with those found in the open literature for the same loading conditions. |
|---|---|
| Autores principais: | Nogueira, F. |
| Outros Autores: | Cunha, J.; Mateus, A.; Malça, C.; Costa, J. D.; Branco, R. |
| Assunto: | Low-cycle fatigue cyclic plastic behaviour strain-softening aluminium alloy 7075-T651 |
| Ano: | 2020 |
| País: | Portugal |
| Tipo de documento: | comunicação em conferência |
| Tipo de acesso: | acesso aberto |
| Instituição associada: | Instituto Politécnico de Leiria |
| Idioma: | inglês |
| Origem: | IC-online |
| Resumo: | This paper aims at studying the cyclic plastic behaviour of the 7075-T651 aluminium alloy under fully-reversed strain-controlled conditions. Tests are conducted under strain-control mode, at room temperature, in a conventional servo-hydraulic machine, from smooth samples, using the single step method, with strain amplitudes (∆ε/2) in the range ±0.5 to ±2.75%. This material has exhibited a mixed behaviour, i.e. cyclic strain-hardens at higher strain amplitudes (∆ε/2/>1.1%) and cyclic strain-softens at lower strain amplitudes (∆ε/2<1.1%). A linear relationship between the degree of cyclic strain-hardening and the strain amplitude has been established for higher strain amplitudes. Fatigue-ductility and fatigue-strength properties agree with those found in the open literature for the same loading conditions. |
|---|