Highly Conducting Bombyx mori Silk Fibroin-Based Electrolytes Incorporating Glycerol, Dimethyl Sulfoxide and [Bmim]PF6
| Resumo: | Green, transparent and flexible electrolyte films composed of a Bombyx mori silk fibroin (SF) host biopolymer doped with glycerol (G), dimethyl sulfoxide (DMSO, D) and 1-butyl-3-methylimidazolium hexafluorophosphate ([Bmim]PF6) ionic liquid (IL), were synthesized. The materials were represented by the notation SF@GD@ILx (x = 15, 20 and 30 is the mass ratio of SF/[Bmim]PF6 in %). SF@, SF@G, SF@D and SF@GD samples were also prepared. DMSO was found to play a dual-role, acting as solvent of [Bmim]PF6, and enhancing ionic conductivity. DMSO, alone or combined with [Bmim]PF6, led to the increase of the mean roughness and induced the formation of more ordered Silk II conformations (β-sheets). No structural modifications were detected in the SF@GD@ILx samples upon increasing the temperature up to 100 °C. The highest ionic conductivity was exhibited by the IL-rich sample SF@GD@IL30 (1.07 and 4.61 mS cm−1, at 22 and 100 °C, respectively). In the [Bmim]PF6-doped electrolytes "free" and coordinated PF6− ions coexist. The weight losses occurring below 200 °C involved essentially the release of adsorbed water and DMSO. The suitable mechanical properties, high ionic conductivity and good electrochemical stability suggest that these electrolytes are attractive candidates for application in electrochemical devices. |
|---|---|
| Autores principais: | Fernandes, Tânia C. D. |
| Outros Autores: | Gonçalves, Helena M R; Paz, Filipe A. A.; Sousa, Joana F. M.; Valente, Artur J. M.; Silva, Maria M.; Zea Bermudez, Verónica de; Pereira, Rui F. P. |
| Assunto: | Bombyx mori silk fibroin (SF) [Bmim]PF6 |
| Ano: | 2020 |
| País: | Portugal |
| Tipo de documento: | artigo |
| Tipo de acesso: | acesso aberto |
| Instituição associada: | Instituto Politécnico do Porto |
| Idioma: | inglês |
| Origem: | Repositório Científico do Instituto Politécnico do Porto |
| Resumo: | Green, transparent and flexible electrolyte films composed of a Bombyx mori silk fibroin (SF) host biopolymer doped with glycerol (G), dimethyl sulfoxide (DMSO, D) and 1-butyl-3-methylimidazolium hexafluorophosphate ([Bmim]PF6) ionic liquid (IL), were synthesized. The materials were represented by the notation SF@GD@ILx (x = 15, 20 and 30 is the mass ratio of SF/[Bmim]PF6 in %). SF@, SF@G, SF@D and SF@GD samples were also prepared. DMSO was found to play a dual-role, acting as solvent of [Bmim]PF6, and enhancing ionic conductivity. DMSO, alone or combined with [Bmim]PF6, led to the increase of the mean roughness and induced the formation of more ordered Silk II conformations (β-sheets). No structural modifications were detected in the SF@GD@ILx samples upon increasing the temperature up to 100 °C. The highest ionic conductivity was exhibited by the IL-rich sample SF@GD@IL30 (1.07 and 4.61 mS cm−1, at 22 and 100 °C, respectively). In the [Bmim]PF6-doped electrolytes "free" and coordinated PF6− ions coexist. The weight losses occurring below 200 °C involved essentially the release of adsorbed water and DMSO. The suitable mechanical properties, high ionic conductivity and good electrochemical stability suggest that these electrolytes are attractive candidates for application in electrochemical devices. |
|---|