Compressive strength at high temperatures of a concrete made with recycled tire textile and steel fibers
| Resumo: | This paper presents the results of a research work on the evaluation of the compressive strength at high temperatures of a concrete made with recycled tire steel and textile fibers. It was considered five different concrete compositions, with a water/cement ratio (W/C = 0.43), differ only in the type and amount of fibers. The compositions with smaller amounts of textile fibers were those that gave better results. The compositions with steel fibers showed a less explosive rupture showing the effectiveness of this type of fibers in the spalling and cracking control. |
|---|---|
| Autores principais: | Santos, C.C. |
| Outros Autores: | Rodrigues, João Paulo |
| Assunto: | Concrete Textile Steel Fiber Tire High temperatures Compressive strength |
| Ano: | 2013 |
| País: | Portugal |
| Tipo de documento: | documento de conferência |
| Tipo de acesso: | acesso aberto |
| Instituição associada: | Instituto Politécnico de Castelo Branco |
| Idioma: | inglês |
| Origem: | Repositório Científico do Instituto Politécnico de Castelo Branco |
| Resumo: | This paper presents the results of a research work on the evaluation of the compressive strength at high temperatures of a concrete made with recycled tire steel and textile fibers. It was considered five different concrete compositions, with a water/cement ratio (W/C = 0.43), differ only in the type and amount of fibers. The compositions with smaller amounts of textile fibers were those that gave better results. The compositions with steel fibers showed a less explosive rupture showing the effectiveness of this type of fibers in the spalling and cracking control. |
|---|