Publicação
New modified Nafion-bisphosphonic acid composite membranes for enhanced proton conductivity and PEMFC performance
| Resumo: | ABSTRACT: Proton exchange membranes remain a crucial material and a key challenge to fuel cell science and technology. In this work, new Nafion membranes are prepared by a casting method using aryl- or azaheteroaromatic bisphosphonate compounds as dopants. The incorporation of the dopant, considered at 1 wt% loading after previous selection, produces enhanced proton conductivity properties in the new membranes, at different temperature and relative humidity conditions, in comparison with values obtained with commercial Nafion. Water uptake and ionic exchange capacity (IEC) are also assessed due to their associated impact on transport properties, resulting in superior values than Nafion when tested in the same experimental conditions. These improvements by doped membranes prompted the evaluation of their potential application in fuel cells, at different temperatures. The new membranes, in membrane-electrode assemblies (MEAs), show an increased fuel cell maximum power output with temperature until 60 degrees C or 70 degrees C, followed by a decrease above these temperatures, a Nafion-like behaviour when measured in the same conditions. The membrane doped with [1,4-phenylenebis(hydroxymethanetriyl)] tetrakis(phosphonic acid) (BP2) presents better results than Nafion N-115 membrane at all studied temperatures, with a maximum power output performance of similar to 383 mW cm(-2) at 70 degrees C. Open circuit potentials of the fuel cell were always higher than values obtained for Nafion MEAs in all studied conditions, indicating the possibility of advantageous restrain to gas crossover in the new doped membranes. |
|---|---|
| Autores principais: | Teixeira, Fatima |
| Outros Autores: | de Sá, A.I.; Teixeira, António P. S.; Ortiz-Martínez, V. M.; Ortiz, A.; Ortiz, Inmaculada; Rangel, C. M. |
| Assunto: | Fuel cells Proton exchange membrane Polymer electrolyte membrane Nafion Bisphosphonates |
| Ano: | 2021 |
| País: | Portugal |
| Tipo de documento: | artigo |
| Tipo de acesso: | acesso aberto |
| Instituição associada: | Laboratório Nacional de Energia e Geologia, I.P. |
| Idioma: | inglês |
| Origem: | Repositório do LNEG |
| Resumo: | ABSTRACT: Proton exchange membranes remain a crucial material and a key challenge to fuel cell science and technology. In this work, new Nafion membranes are prepared by a casting method using aryl- or azaheteroaromatic bisphosphonate compounds as dopants. The incorporation of the dopant, considered at 1 wt% loading after previous selection, produces enhanced proton conductivity properties in the new membranes, at different temperature and relative humidity conditions, in comparison with values obtained with commercial Nafion. Water uptake and ionic exchange capacity (IEC) are also assessed due to their associated impact on transport properties, resulting in superior values than Nafion when tested in the same experimental conditions. These improvements by doped membranes prompted the evaluation of their potential application in fuel cells, at different temperatures. The new membranes, in membrane-electrode assemblies (MEAs), show an increased fuel cell maximum power output with temperature until 60 degrees C or 70 degrees C, followed by a decrease above these temperatures, a Nafion-like behaviour when measured in the same conditions. The membrane doped with [1,4-phenylenebis(hydroxymethanetriyl)] tetrakis(phosphonic acid) (BP2) presents better results than Nafion N-115 membrane at all studied temperatures, with a maximum power output performance of similar to 383 mW cm(-2) at 70 degrees C. Open circuit potentials of the fuel cell were always higher than values obtained for Nafion MEAs in all studied conditions, indicating the possibility of advantageous restrain to gas crossover in the new doped membranes. |
|---|