Gold deposition from 1-butyl-1-methyl-pyrrolidinium dicyanamide ionic liquid at open-circuit and under potentiostatic control
| Resumo: | In this work, the deposition of gold on copper substrates from solutions of HAuCl4.3H2O in 1-butyl-1-methylpyrrolidinium dicyanamide was studied. Deposition was carried out in open-circuit and under potentiostatic control at temperatures from 293 to 353 K, in normal atmosphere, with deposition conditions allowing water from atmospheric absorption up to 0.8 wt.%. Films of gold were obtained by both methods. Deposition at open-circuit occurs by galvanic displacement mechanism. Involvement of Cu+ species in the electrodeposition process was suggested by cyclic voltammetry. Furthermore, copper incorporation in the gold films was confirmed by X-ray diffraction. SEM observation and XRD analysis show that films are nanocrystalline with a globular morphology except for the films formed under potentiostatic control at 353 K, which show a dendritic structure. The size of the crystallites determined by Scherrer's equation varies in the range from 6 to 25 nm. |
|---|---|
| Autores principais: | Sá, A.I. De |
| Outros Autores: | Eugénio, S.; Quaresma, S.; Rangel, C. M.; Vilar, R. |
| Assunto: | Gold Electrodeposition Ionic liquids Open-circuit deposition |
| Ano: | 2013 |
| País: | Portugal |
| Tipo de documento: | artigo |
| Tipo de acesso: | acesso aberto |
| Instituição associada: | Laboratório Nacional de Energia e Geologia, I.P. |
| Idioma: | inglês |
| Origem: | Repositório do LNEG |
| Resumo: | In this work, the deposition of gold on copper substrates from solutions of HAuCl4.3H2O in 1-butyl-1-methylpyrrolidinium dicyanamide was studied. Deposition was carried out in open-circuit and under potentiostatic control at temperatures from 293 to 353 K, in normal atmosphere, with deposition conditions allowing water from atmospheric absorption up to 0.8 wt.%. Films of gold were obtained by both methods. Deposition at open-circuit occurs by galvanic displacement mechanism. Involvement of Cu+ species in the electrodeposition process was suggested by cyclic voltammetry. Furthermore, copper incorporation in the gold films was confirmed by X-ray diffraction. SEM observation and XRD analysis show that films are nanocrystalline with a globular morphology except for the films formed under potentiostatic control at 353 K, which show a dendritic structure. The size of the crystallites determined by Scherrer's equation varies in the range from 6 to 25 nm. |
|---|