Effect of ionic liquid anion and cation on the physico-chemical properties of poly(vinylidene fluoride)/ionic liquid blends
| Resumo: | Poly(vinylidene fluoride), PVDF, has been blended with different ionic liquids (IL) in order to evaluate the effect of the different IL anions and cations on the electroative -phase, thermal, mechanical and electrical properties of the polymer blend. [C2MIM][Cl], [C6MIM][Cl], [C10MIM][Cl], [C2MIM][NTf2], [C6MIM][NTf2], [C10MIM][NTf2] have been selected and were introduced in the polymer at a weight percentage of 40 wt%. It was found that the incorporation of ILs into the PVDF matrix leads to an increase of the -phase content due to the strong electrostatic interactions between the dipolar moments of PVDF and the ILs. Further, the incorporation of ILs into PVDF strongly decreases the elastic modulus and increases the electrical conductivity of the blend with respect to the pure polymer matrix, all these effects being accompanied by a modification of the crystallization kinetics, as indicated by the modified spherulitic microstructure. Thus, novel PVDF/IL blends films with high transparency, excellent antistatic properties, and highly polar crystal form fraction were successfully achieved. |
|---|---|
| Autores principais: | Mejri, R. |
| Outros Autores: | Dias, J. C.; Lopes, A. C.; Bebes Hentati, S.; Silva, Maria Manuela; Botelho, Gabriela; Mão De Ferro, A.; Esperança, J. M. S. S.; Maceiras, A.; Laza, J. M.; Vilas, J. L.; León, L. M.; Lanceros-Méndez, S. |
| Assunto: | Ionic liquids Polymer composites Electroactive polymers Poly(vinylidene fluoride) Ciências Naturais::Ciências Físicas Ciências Naturais::Ciências Químicas |
| Ano: | 2015 |
| País: | Portugal |
| Tipo de documento: | artigo |
| Tipo de acesso: | acesso restrito |
| Instituição associada: | Universidade do Minho |
| Idioma: | inglês |
| Origem: | RepositóriUM - Universidade do Minho |
| Resumo: | Poly(vinylidene fluoride), PVDF, has been blended with different ionic liquids (IL) in order to evaluate the effect of the different IL anions and cations on the electroative -phase, thermal, mechanical and electrical properties of the polymer blend. [C2MIM][Cl], [C6MIM][Cl], [C10MIM][Cl], [C2MIM][NTf2], [C6MIM][NTf2], [C10MIM][NTf2] have been selected and were introduced in the polymer at a weight percentage of 40 wt%. It was found that the incorporation of ILs into the PVDF matrix leads to an increase of the -phase content due to the strong electrostatic interactions between the dipolar moments of PVDF and the ILs. Further, the incorporation of ILs into PVDF strongly decreases the elastic modulus and increases the electrical conductivity of the blend with respect to the pure polymer matrix, all these effects being accompanied by a modification of the crystallization kinetics, as indicated by the modified spherulitic microstructure. Thus, novel PVDF/IL blends films with high transparency, excellent antistatic properties, and highly polar crystal form fraction were successfully achieved. |
|---|