| Resumo: | This paper reports experimental results of 32 hybrid cement mixes regarding the joint effect of sodium hydroxide concentration, the use of a commercial superplasticizer and a biopolymer on the flow and compressive strength performance. The results show that the use of commercial admixtures led to a slightly increase in the flow of mortars with lower sodium hydroxide concentration. A mixture based on 80% fly ash, 10% calcium hydroxide and 10% waste glass showed the highest compressive strength. A compressive strength decrease was noticed concerning the use of the two admixtures that can due to the fact that those admixtures are not stable on high basic media. |
|---|---|
| Autores principais: | Abdollahnejad, Zahra |
| Outros Autores: | Kheradmand, Mohammad; Pacheco-Torgal, F. |
| Assunto: | Biopolymer Flow Fly ash Hybrid cement Polycarboxylate Waste glass Waste reuse |
| Ano: | 2017 |
| País: | Portugal |
| Tipo de documento: | comunicação em conferência |
| Tipo de acesso: | acesso aberto |
| Instituição associada: | Universidade do Minho |
| Idioma: | inglês |
| Origem: | RepositóriUM - Universidade do Minho |
| Resumo: | This paper reports experimental results of 32 hybrid cement mixes regarding the joint effect of sodium hydroxide concentration, the use of a commercial superplasticizer and a biopolymer on the flow and compressive strength performance. The results show that the use of commercial admixtures led to a slightly increase in the flow of mortars with lower sodium hydroxide concentration. A mixture based on 80% fly ash, 10% calcium hydroxide and 10% waste glass showed the highest compressive strength. A compressive strength decrease was noticed concerning the use of the two admixtures that can due to the fact that those admixtures are not stable on high basic media. |
|---|