New insights into the degradation mechanism of cellulose nitrate in cinematographic films by Raman microscopy
| Resumo: | The degradation of cellulose nitrate cinematographic films stored inside an aluminum can was studied by infrared spectroscopy and Raman microscopy. Cellulose nitrate image heritage is strongly susceptible to degradation, being a major conservation challenge. Infrared spectroscopy has been the traditional technique in the assessment of the polymer degradation, but new in situ diagnostic tools to monitor the initial stages of degradation are needed. In this work, cellulose nitrate films were produced and irradiated as aging references to understand how chemical changes were observed in Raman spectroscopy. In comparison with infrared spectroscopy, this technique confirmed the mechanisms proposed in the literature and, at advanced stages of degradation, provided new relevant information detecting an intense peak at 1046 cm −1 associated to nitric acid. Comparing these results with the cinematographic films, it was observed that the plasticizers, which identification was more straightforward using Raman microscopy, have contributions in the regions were chemical changes occur, making it difficult to draw conclusions. Nevertheless, nitric acid and silver nitrate peaks were found in Raman spectra confirming the unstable and noxious environment inside de aluminum can and proving that Raman microscopy can be a valuable complementary in situ technique for cellulose nitrate degradation studies. |
|---|---|
| Autores principais: | Neves, Artur |
| Outros Autores: | Angelin, Eva Mariasole; Roldão, Élia; Melo, Maria João |
| Assunto: | celluloid cellulose nitrate cinematographic films degradation mechanisms photooxidation General Materials Science Spectroscopy |
| Ano: | 2019 |
| País: | Portugal |
| Tipo de documento: | artigo |
| Tipo de acesso: | acesso aberto |
| Instituição associada: | Universidade Nova de Lisboa |
| Idioma: | inglês |
| Origem: | Repositório Institucional da UNL |
| Resumo: | The degradation of cellulose nitrate cinematographic films stored inside an aluminum can was studied by infrared spectroscopy and Raman microscopy. Cellulose nitrate image heritage is strongly susceptible to degradation, being a major conservation challenge. Infrared spectroscopy has been the traditional technique in the assessment of the polymer degradation, but new in situ diagnostic tools to monitor the initial stages of degradation are needed. In this work, cellulose nitrate films were produced and irradiated as aging references to understand how chemical changes were observed in Raman spectroscopy. In comparison with infrared spectroscopy, this technique confirmed the mechanisms proposed in the literature and, at advanced stages of degradation, provided new relevant information detecting an intense peak at 1046 cm −1 associated to nitric acid. Comparing these results with the cinematographic films, it was observed that the plasticizers, which identification was more straightforward using Raman microscopy, have contributions in the regions were chemical changes occur, making it difficult to draw conclusions. Nevertheless, nitric acid and silver nitrate peaks were found in Raman spectra confirming the unstable and noxious environment inside de aluminum can and proving that Raman microscopy can be a valuable complementary in situ technique for cellulose nitrate degradation studies. |
|---|