High-performance wide bandgap perovskite solar cells fabricated in ambient high-humidity conditions
| Resumo: | Lead-halide perovskite solar cells (PSCs) are currently the most promising emergent thin-film photovoltaic technology, having already reached power conversion efficiency (PCE) levels of state-of-the-art wafer-based silicon cells. The class of wide bandgap PSCs has also demonstrated high PCE values, thus becoming highly attractive for top sub-cells in tandem devices constructed with silicon or other types of bottom sub-cells. In this study, wide bandgap double-halide (Cs0.17FA0.83PbI3-xBrx) perovskite absorbers were developed with different bromine content, aiming to obtain bandgap values between 1.66 to 1.74 eV, by a glovebox-free (ambient) procedure. Low-cost inorganic materials, i.e. TiO2 and CuSCN, were used for the electron and hole transport layers, respectively. The 1.70 eV bandgap perovskite resulted in the highest reproducibility and stability (>80% initial PCE after 3500 hours) properties of the PSCs, remarkably attaining 16.4% PCE even with ambient and high humidity (∼70%) fabrication conditions. This journal is |
|---|---|
| Autores principais: | Menda, Ugur Deneb |
| Outros Autores: | Ribeiro, Guilherme; Nunes, Daniela; Calmeiro, Tomás; Águas, Hugo; Fortunato, Elvira; Martins, Rodrigo; Mendes, Manuel J. |
| Assunto: | General Materials Science Chemistry (miscellaneous) SDG 7 - Affordable and Clean Energy |
| Ano: | 2021 |
| País: | Portugal |
| Tipo de documento: | artigo |
| Tipo de acesso: | acesso aberto |
| Instituição associada: | Universidade Nova de Lisboa |
| Idioma: | inglês |
| Origem: | Repositório Institucional da UNL |
| Resumo: | Lead-halide perovskite solar cells (PSCs) are currently the most promising emergent thin-film photovoltaic technology, having already reached power conversion efficiency (PCE) levels of state-of-the-art wafer-based silicon cells. The class of wide bandgap PSCs has also demonstrated high PCE values, thus becoming highly attractive for top sub-cells in tandem devices constructed with silicon or other types of bottom sub-cells. In this study, wide bandgap double-halide (Cs0.17FA0.83PbI3-xBrx) perovskite absorbers were developed with different bromine content, aiming to obtain bandgap values between 1.66 to 1.74 eV, by a glovebox-free (ambient) procedure. Low-cost inorganic materials, i.e. TiO2 and CuSCN, were used for the electron and hole transport layers, respectively. The 1.70 eV bandgap perovskite resulted in the highest reproducibility and stability (>80% initial PCE after 3500 hours) properties of the PSCs, remarkably attaining 16.4% PCE even with ambient and high humidity (∼70%) fabrication conditions. This journal is |
|---|