| Resumo: | The inhibition efficiency (IE) of K3[Fe(CN)6] in controlling corrosion of carbon steel in aqueous solution containing 60 ppm of Cl- in the presence and absence of Zn2+ has been evaluated by weight loss method. The formulation consisting of 100 ppm K3[Fe(CN)6] and 50 ppm Zn2+ offers 98% inhibition efficiency to carbon steel immersed in aqueous solution containing 60 ppm Cl-. A synergistic effect exists between K3[Fe(CN)6] and Zn2+. As immersion period increases, the inhibition efficiency of K3[Fe(CN)6]─ Zn2+ system decreases. Polarization study reveals that this formulation controls the cathodic reaction predominantly. AC impedance spectra reveal that a protective film is formed on the metal surface. FTIR spectra reveal that the protective film consists of Prussian blue and Zn(OH)2. The film is found to be UV fluorescent. |
|---|
| Autores principais: | Kalaivani,R. |
|---|
| Outros Autores: | Narayanaswamy,B.; Selvi,J. A.; Amalraj,A. J.; Jeyasundari,J.; Rajendran,S. |
|---|
| Assunto: | corrosion inhibition carbon steel Prussian blue synergistic effect |
|---|
| Ano: | 2009 |
|---|
| País: | Portugal |
|---|
| Tipo de documento: | artigo |
|---|
| Tipo de acesso: | acesso aberto |
|---|
| Instituição associada: | Fundação para a Ciência e Tecnologia |
|---|
| Idioma: | inglês |
|---|
| Origem: | SciELO Portugal |
|---|