Adhesion of dental sealants to enamel with self-etching adhesives in salivar contamination conditions: Influence of the light curing protocol
| Resumo: | Purpose: To evaluate the influence of the light curing protocol in the shear bond strength of a sealant to enamel treated with two self-etching adhesive systems, in salivary contamination conditions. Materials and Methods: The dental sealant (Delton, Dentsply) was applied, after saliva contamination, onto the vestibular enamel of sixty human incisors treated with Xeno III (Dentsply) or Prompt-L-Pop (3M/Espe). These two groups were further divided into two subgroups (n = 15) according to the curing time: 1) the adhesive system was cured with the sealant (co-polymerization), and 2) adhesive and sealant were light cured independently (independent polymerization). After the adhesive procedures, specimens were stored in water (37 °C–24 h) and thermal-cycled. Shear bond strength tests were done in an universal testing machine. Data was analyzed with two-way ANOVA. Results: There were no statistical differences (p = 0.267) between the adhesive systems tested. The co-polymerization groups (33.3 ± 9.4 MPa) yielded statistically higher shear bond strength values than the independent polymerization groups (28.2 ± 4.7 MPa). Even with saliva contamination, the self-etching adhesive systems used yielded high shear bond strength values. Conclusions: In the conditions tested, the co-polymerization of the adhesive systems with the sealant led to higher bond strength values to enamel than the independent polymerization. |
|---|---|
| Autores principais: | Chasqueira, Filipa |
| Outros Autores: | Portugal, Jaime; Oliveira, Sofia Santos Arantes e; Lopes, Luís Pires |
| Assunto: | Fissure sealant Saliva contamination Self-etching adhesive systems Light cure |
| Ano: | 2011 |
| País: | Portugal |
| Tipo de documento: | artigo |
| Tipo de acesso: | acesso aberto |
| Instituição associada: | Universidade de Lisboa |
| Idioma: | inglês |
| Origem: | Repositório da Universidade de Lisboa |
| Resumo: | Purpose: To evaluate the influence of the light curing protocol in the shear bond strength of a sealant to enamel treated with two self-etching adhesive systems, in salivary contamination conditions. Materials and Methods: The dental sealant (Delton, Dentsply) was applied, after saliva contamination, onto the vestibular enamel of sixty human incisors treated with Xeno III (Dentsply) or Prompt-L-Pop (3M/Espe). These two groups were further divided into two subgroups (n = 15) according to the curing time: 1) the adhesive system was cured with the sealant (co-polymerization), and 2) adhesive and sealant were light cured independently (independent polymerization). After the adhesive procedures, specimens were stored in water (37 °C–24 h) and thermal-cycled. Shear bond strength tests were done in an universal testing machine. Data was analyzed with two-way ANOVA. Results: There were no statistical differences (p = 0.267) between the adhesive systems tested. The co-polymerization groups (33.3 ± 9.4 MPa) yielded statistically higher shear bond strength values than the independent polymerization groups (28.2 ± 4.7 MPa). Even with saliva contamination, the self-etching adhesive systems used yielded high shear bond strength values. Conclusions: In the conditions tested, the co-polymerization of the adhesive systems with the sealant led to higher bond strength values to enamel than the independent polymerization. |
|---|